立方氮化硼砂带磨削性能的研究

doi: 10.13394/j.cnki.jgszz.2017.5.0009

肖乐银^1,2,3,
陈家荣^1,2,
林峰^1,2,3,
谢志刚^1,2,3,
谢德龙^2,3,
陈超^1,2,3

1. 广西超硬材料重点实验室, 桂林 541004;
2. 国家特种矿物材料工程技术研究中心, 桂林 541004;
3. 中国有色桂林矿产地质研究院有限公司, 桂林 541004

基金项目:

桂林市科学研究与技术开发计划（2016010701-1）；广西超硬材料重点实验室专项经费。

详细信息

作者简介:
肖乐银,男,1981年生,硕士、高级工程师。主要从事超硬材料磨具的研究与开发。E-mail:xiaoleyin2005@163.com

中图分类号: TG74;TQ164
计量
- 文章访问数: 158
- HTML全文浏览量: 25
- PDF下载量: 5
- 被引次数: 0
出版历程
- 修回日期: 2017-08-07
- 网络出版日期: 2022-07-27

Research on grinding performance of CBN abrasive belt

XIAO Leyin^1,2,3,
CHEN Jiarong^1,2,
LIN Feng^1,2,3,
XIE Zhigang^1,2,3,
XIE Delong^2,3,
CHEN Chao^1,2,3

1. Guangxi Key Laboratory of Superhard Materials, Guilin 541004, China;
2. National Special Mineral Material Engineering Research Center, Guilin 541004, China;
3. China Nonferrous Metal(Guilin) Geology And Mining Co., Ltd., Guilin 541004, China

摘要

摘要: 用相同粒度的CBN与刚玉砂带，分别磨削45号钢，分析并比较其磨削性能。结果表明：CBN砂带磨耗比为210.4，刚玉砂带磨耗比为18.9，CBN砂带耐磨性远远高于刚玉砂带；CBN砂带加工工件的表面质量要优于刚玉砂带，但两者磨削工件的表面粗糙度R_a相差不大，分别为0.127 μm、0.128 μm；CBN砂带磨料出刃高，初始磨削效率高；刚玉砂带树脂结合剂硬度低，磨削60 min后基本丧失了磨削能力，而CBN砂带金属镍结合剂与磨料硬度有很好的匹配性，180 min后仍能保持28.2 g/h磨削效率。
- CBN砂带 /
- 磨耗比 /
- 表面粗糙度 /
- 磨削效率
Abstract: CBN and corundum belts, at the same granularity, were used to grind 45 steel.Their grinding performance were analyzed and compared.Resultsshow that the grinding ratios of CBN belt and corundum belt are 210.4 and 18.9, respectively, which means that the wear resistance of CBN belt is better than that of corundum abrasive belt.It is also found that CBN belt does better than corundum belt in the surface quality of grinding workpiece, while the surface roughness R_a of the workpiece are almost the same, respectively 0.127 μm and 0.128 μm, and that the abrasive protrusion of CBN belt is higher, leading to superior initial grinding efficiency.In addition, the hardness of resin bond in corundum belt is small, which basically loses the grinding ability after grinding for 60 minutes, but nickel metal bond in CBN belt matches well with CBN abrasive, so that CBN belt could keep 28.2 g/h grinding efficiency after 180 minutes.
- CBN abrasive belt /
- abrasive grinding ratio /
- surface roughness /
- grinding efficiency