Application of porous CBN/Cu-Sn-Zn agglomerated abrasive in rail grinding wheel
-
摘要: 为提高钢轨打磨砂轮的磨削效率和使用寿命,制备一种表面多孔但内部紧实的CBN/Cu-Sn-Zn堆积磨料。讨论Cu-Sn-Zn结合剂的性能、孔隙结构对CBN堆积磨料的影响以及堆积磨料对砂轮结构强度的影响,并通过钢轨被动打磨试验,对堆积磨料添加前后砂轮的磨削效果进行评价。试验结果表明:最佳的多孔CBN堆积磨料试样弯曲强度为78.5 MPa,抗冲击强度为5.5 kJ/m2,表面孔隙率在30%~40%。磨料的复合使用可以有效地结合CBN高硬度与锆刚玉良好的冲击韧性的特点,添加体积分数为20%的堆积磨料提高钢轨打磨砂轮的打磨效率及打磨质量。Abstract: To improve the grinding efficiency and service life of rail grinding wheels, a surface porous CBN/Cu-Sn-Zn compact abrasive is prepared. This work discussed the performance of Cu-Sn metal bond used for preparing agglomerated abrasives, the influence of pore structure on CBN agglomerated abrasive and the effect of agglomerated abrasive on the structural strength of grinding wheel. The grinding effect of grinding wheel before and after compound abrasive addition was evaluated by rail grinding experiment. The results show that the best porous CBN agglomerated abrasive sample has a flexural strength of 78.5 MPa, an impact strength of 5.5 kJ/m2, and a surface porosity of 30%~40%. The combined use of abrasive can effectively combine the high hardness of CBN with the good impact toughness of zirconium corundum. The grinding efficiency and grinding quality of rail grinding wheels with 20% volume concentration accumulated abrasives are further improved.
-
表 1 打磨的钢轨工件元素成分
Table 1. Element compositions of the ground rail workpiece
元素 质量分数 ω / % C 0.650~0.760 Si 0.150~0.580 Mn 0.700~1.200 P ≤ 0.035 S ≤ 0.030 V 0.030 Nb ≤ 0.010 Fe 余量 -
[1] 龚继军, 郭猛刚, 侯博, 等. 钢轨打磨技术发展现状及打磨策略探讨 [J]. 机车电传动,2020(3):23-29, 34.GONG Jijun, GUO Menggang, HOU Bo, et al. Discussion on rail grinding technology development situation and grind strategies [J]. Electric Drive For Locomotives,2020(3):23-29, 34. [2] 樊文刚, 刘月明, 李建勇. 高速铁路钢轨打磨技术的发展现状与展望 [J]. 机械工程学报,2018,54(22):184-193. doi: 10.3901/JME.2018.22.184FAN Wengang, LIU Yueming, LI Jianyong. Development status and prospect of rail grinding technology for high speed railway [J]. Chinese Journal of Mechanical Engineering,2018,54(22):184-193. doi: 10.3901/JME.2018.22.184 [3] 窦礼云. 新型复合砂轮高效打磨钢轨的性能研究 [D]. 南京: 南京航空航天大学, 2019.DOU Liyun. Study on the performance of high efficiency grinding for grinding rail with new composite grinding wheel [D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2019. [4] ZHANG W, ZHANG P, ZHANG J, et al. Probing the effect of abrasive grit size on rail grinding behaviors [J]. Journal of Manufacturing Processes,2020,53:388-395. doi: 10.1016/j.jmapro.2020.03.028 [5] WANG R, ZHOU K, YANG J, et al. Effects of abrasive material and hardness of grinding wheel on rail grinding behaviors [J]. Wear,2020,454-455:203332. doi: 10.1016/j.wear.2020.203332 [6] WU Y, SHEN M, QU M, et al. An experimental investigation on surface layer damage in high-efficiency and low-damage grinding of rail by slotted CBN grinding wheel [J]. The International Journal of Advanced Manufacturing Technology,2019,105(7/8):2833-2841. doi: 10.1007/s00170-019-04528-x [7] YUAN Y J, ZHANG W L, ZHANG P, et al. Porous grinding wheels toward alleviating the pre-fatigue and increasing the material removal efficiency for rail grinding [J]. Tribology International,2021,154:106692. doi: 10.1016/j.triboint.2020.106692 [8] LIU P, ZOU W, PENG J, et al. Study on the effect of grinding pressure on material removal behavior performed on a self-designed passive grinding simulator [J]. Applied Sciences,2021,11(9)-4128. doi: 10.3390/app11094128 [9] 李端. 高铁钢轨滚磨参数对磨削性能的影响研究 [D]. 郑州: 河南工业大学, 2020.LI Duan. Research on the influence of high speed rail rolling parameters on grinding performance [D]. Zhengzhou: Henan University of Technology, 2020. [10] 左宏森. 超硬材料烧结制品 [M]. 郑州: 郑州大学出版社, 2017.ZUO Hongsen. Super hard material sintered products [M]. Zhengzhou: Zhengzhou University Press, 2017. [11] 韩平. 金刚石珩磨抛光油石结合剂结构和性能及其珩磨应用 [D]. 秦皇岛: 燕山大学, 2013.HAN Ping. Study on the performance of high efficiency grinding for grinding rail with new composite grinding wheel [D]. Qinhuangdao: Yanshan University, 2013. [12] 赵亚庆, 何方. 孔隙率对多孔金属结合剂金刚石节块性能的影响 [J]. 超硬材料工程,2015,27(5):18-23. doi: 10.3969/j.issn.1673-1433.2015.05.004ZHAO Yaqing, HE Fang. Influence of porosity on the performances of porous metal-bond diamond blocks [J]. Super Hard Materials Engineering,2015,27(5):18-23. doi: 10.3969/j.issn.1673-1433.2015.05.004 [13] ZHAO B, DING W, CHEN Z, et al. Pore structure design and grinding performance of porous metal-bonded CBN abrasive wheels fabricated by vacuum sintering [J]. Journal of Manufacturing Processes, 2019, 44: 125-132. -